WMB-PE7015P LLDPE White Masterbatch with 50% Rutile Titanium Dioxide for Bright Whiteness and Slightly Bluish Undertone

全カテゴリー

アルコールエステル

連絡ください

Ms. jojo

jojo@tinoxchem.com

+8618628936904

今連絡してください

WMB-PE7015P LLDPE White Masterbatch with 50% Rutile Titanium Dioxide for Bright Whiteness and Slightly Bluish Undertone

ブランド名:	TINOX
モデル番号:	WMB-PE7015P
支払条件:	L/C、D/A、D/P、T/T

起源の場所:

ハイライト:

Slightly Bluish Undertone White Masterbatch

LLDPE White Masterbatch

製品説明

WMB-PE7015P LLDPE White Masterbatch with 50% Rutile Titanium Dioxide for Bright Whiteness and Slightly Bluish Undertone

WMB-PE7015P LLDPE White Masterbatch

WMB-PE7015P is a premium-grade white masterbatch containing 70% finely dispersed rutile titanium dioxide in an LLDPE carrier resin. This high-concentration formulation delivers exceptional opacity and whiteness, making it ideal for demanding plastic processing applications including blown and cast films, extruded sheets, and injection or blow molded parts.

Key Features & Benefits

Superior Opacity: High 70% TiO2 content provides excellent covering power
Easy Processing: Optimized flow characteristics for smooth production
Fine Pellet Size: Ensures uniform dispersion and consistent results
Light Bluish Undertone: Delivers bright, appealing whiteness
Versatile Application: Suitable for films, sheets, and molded components

Product Specification

Physical Properties	Average Value
Appearance	White granule
Polyethylene Carrier (LLDPE) (%)	15.5
Rutile Titanium Dioxide (%)	70.0
Ground Calcium Carbonate (%)	10.0
PE Wax (%)	4.5
Specific Gravity	1.9
Melt Flow Rate (MFR, G/10Min)	14.0
Bulk Density (g/100cc)	115
Pellet Size (Pellets/g)	580
Moisture Content (%, Max.)	0.5

Recommended Processing Conditions

Parameter	Specification
Injection Pressure	75-110 MPa
Melt Temperature	190~225℃
Mold Temperature	30~70℃
Drying	3hr @ 80~85℃

タグ:

Slightly Bluish Undertone White Masterbatch

LLDPE White Masterbatch

商品の詳細

家へ > 製品 > >

WMB-PE7015P LLDPE White Masterbatch with 50% Rutile Titanium Dioxide for Bright Whiteness and Slightly Bluish Undertone

全カテゴリー

WMB-PE7015P LLDPE White Masterbatch with 50% Rutile Titanium Dioxide for Bright Whiteness and Slightly Bluish Undertone

ブランド名:	TINOX
モデル番号:	WMB-PE7015P
支払条件:	L/C、D/A、D/P、T/T

詳細情報

製品説明

詳細情報

起源の場所:

中国

ブランド名:

TINOX

モデル番号:

WMB-PE7015P

受渡し時間:

5～8日

支払条件:

L/C、D/A、D/P、T/T

ハイライト:

Slightly Bluish Undertone White Masterbatch

LLDPE White Masterbatch

製品説明

WMB-PE7015P LLDPE White Masterbatch with 50% Rutile Titanium Dioxide for Bright Whiteness and Slightly Bluish Undertone

WMB-PE7015P LLDPE White Masterbatch

Key Features & Benefits

Superior Opacity: High 70% TiO2 content provides excellent covering power
Easy Processing: Optimized flow characteristics for smooth production
Fine Pellet Size: Ensures uniform dispersion and consistent results
Light Bluish Undertone: Delivers bright, appealing whiteness
Versatile Application: Suitable for films, sheets, and molded components

Product Specification

Physical Properties	Average Value
Appearance	White granule
Polyethylene Carrier (LLDPE) (%)	15.5
Rutile Titanium Dioxide (%)	70.0
Ground Calcium Carbonate (%)	10.0
PE Wax (%)	4.5
Specific Gravity	1.9
Melt Flow Rate (MFR, G/10Min)	14.0
Bulk Density (g/100cc)	115
Pellet Size (Pellets/g)	580
Moisture Content (%, Max.)	0.5

Recommended Processing Conditions

Parameter	Specification
Injection Pressure	75-110 MPa
Melt Temperature	190~225℃
Mold Temperature	30~70℃
Drying	3hr @ 80~85℃

タグ:

二酸化チタンのルチル

二酸化チタンAnatase

塩化物プロセス二酸化チタン

硫酸塩のプロセス二酸化チタン

二酸化チタンの顔料

二酸化チタンのペンキ

二酸化チタンの粉

TiO2二酸化チタン

セルロースエーテル

アルコール エステル

二酸化チタンのルチル

二酸化チタンAnatase

塩化物プロセス二酸化チタン

硫酸塩のプロセス二酸化チタン

二酸化チタンの顔料

二酸化チタンのペンキ

二酸化チタンの粉

TiO2二酸化チタン

セルロースエーテル

アルコール エステル

商品の詳細

二酸化チタンのルチル

二酸化チタンAnatase

塩化物プロセス二酸化チタン

硫酸塩のプロセス二酸化チタン

二酸化チタンの顔料

二酸化チタンのペンキ

二酸化チタンの粉

TiO2二酸化チタン

セルロースエーテル

アルコール エステル

WMB-PE7015P LLDPE White Masterbatch with 50% Rutile Titanium Dioxide for Bright Whiteness and Slightly Bluish Undertone

Slightly Bluish Undertone White Masterbatch

LLDPE White Masterbatch

Slightly Bluish Undertone White Masterbatch

LLDPE White Masterbatch

商品の詳細

二酸化チタンのルチル

二酸化チタンAnatase

塩化物プロセス二酸化チタン

硫酸塩のプロセス二酸化チタン

二酸化チタンの顔料

二酸化チタンのペンキ

二酸化チタンの粉

TiO2二酸化チタン

セルロースエーテル

アルコール エステル

WMB-PE7015P LLDPE White Masterbatch with 50% Rutile Titanium Dioxide for Bright Whiteness and Slightly Bluish Undertone

Slightly Bluish Undertone White Masterbatch

LLDPE White Masterbatch

Slightly Bluish Undertone White Masterbatch

LLDPE White Masterbatch

アルコールエステル

アルコールエステル

アルコールエステル

アルコールエステル